| About |
|---|
| LUVOCOM® 50/TF/15/BK is a Polycarbonate (PC) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LUVOCOM® 50/TF/15/BK are: Flame Rated High Dimensional Stability Impact Resistant Lubricated Wear Resistant Typical applications include: Engineering/Industrial Parts Business/Office Goods Construction Applications Electrical/Electronic Applications Medical/Healthcare&& |
| Product Description | |
|---|---|
| Supplier | Lehmann |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good Dimensional Stability,Low coefficient of friction,High Heat Resistance,Lubricating,Good wear resistance,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 45 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，5 kg | 40.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.60 to 0.80 | % | DIN 16901 |
| Water absorption rate | |||
| 23℃，24hr | < 0.20 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2200 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 50.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 5.0 | % | ISO 527-2 |
| Bending modulus | 2000 | MPa | ISO 178 |
| bending strength | 80.0 | MPa | ISO 178 |
| Bending strain | 6.0 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 15 | kJ/m² | ISO 179/1eA |
| 23℃ | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1fU | ||
| -30℃ | 80 | kJ/m² | ISO 179/1fU |
| 23℃ | 100 | kJ/m² | ISO 179/1fU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 132 | ℃ | ISO 75-2/A |
| Continuous use temperature | 130 | ℃ | UL 746B |
| Maximum operating temperature | |||
| short-term | 150 | ℃ | |
| Vicat Softening Temp | 160 | ℃ | ISO 306/A |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | DIN 53752 |
| Thermal conductivity coefficient | 0.20 | W/m/K | DIN 52612 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| insulation resistance | > 1.0E+12 | ohms | IEC 60167 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 120 | °C | |
| Drying time – hot air dryer | 4.0 to 6.0 | hr | |
| Barrel rear temperature | 280 to 300 | °C | |
| Barrel middle temperature | 290 to 310 | °C | |
| Barrel front temperature | 300 to 320 | °C | |
| Nozzle temperature | 290 to 310 | °C | |
| Processing (melt) temperature | 295 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |