| About |
|---|
| LUVOCOM® EOG-200 is a Polyetheretherketone (PEEK) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LUVOCOM® EOG-200 are: Flame Rated Chemical Resistant Flame Retardant Lubricated Wear Resistant Typical application of LUVOCOM® EOG-200: Industrial Applications&& |
| Product Description | |
|---|---|
| Supplier | Lehmann |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Flame Characteristics,Lubricating,Good wear resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 380℃，10 kg | 15.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 1.2 to 1.4 | % | DIN 16901 |
| Water absorption rate | |||
| 23℃，24hr | < 0.10 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3900 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 85.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 5.1 | % | ISO 527-2 |
| Bending modulus | 3700 | MPa | ISO 178 |
| bending strength | 140 | MPa | ISO 178 |
| Bending strain | 6.8 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 100 | kJ/m² | ISO 179/1fU |
| 23℃ | 110 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 155 | ℃ | ISO 75-2/A |
| Continuous use temperature | 250 | ℃ | UL 746B |
| Maximum operating temperature | |||
| short-term | 260 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+12 | ohms | IEC 60093 |
| insulation resistance | > 1.0E+12 | ohms | IEC 60167 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Hot air dryer, A | 150 | °C | |
| Hot air dryer, B | 120 | °C | |
| Drying time | |||
| Hot air dryer, A | 3.0 to 6.0 | hr | |
| Hot air dryer, B | 6.0 to 8.0 | hr | |
| Barrel rear temperature | 360 to 370 | °C | |
| Barrel middle temperature | 380 to 390 | °C | |
| Barrel front temperature | 390 to 400 | °C | |
| Nozzle temperature | 360 to 380 | °C | |
| Processing (melt) temperature | 390 | °C | |
| Mold temperature | 170 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Not recognized by UL. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |