| About |
|---|
| Description High Modulus, High Impact, Low Warpage Bio base PA content 24% Application Electric/Electronic Components(LCD Bracket)&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low warping,High impact resistance,Amorphous,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：23℃，3.2 mm | 0.030 to 0.15 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.50 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile strain | |||
| Fracture, 3.20 mm | 6.0 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 13000 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm | 281 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 160 | J/m | ASTM D256 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| 2.50 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 4.0 to 5.0 | hr | |
| Barrel rear temperature | 280 to 300 | °C | |
| Barrel middle temperature | 280 to 300 | °C | |
| Barrel front temperature | 280 to 300 | °C | |
| Nozzle temperature | 280 to 320 | °C | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Back pressure | 29.4 to 58.8 | MPa | |
| Screw speed | 50 to 150 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. 0.20 in/min |
| 4. 0.051 in/min |
| 5. Hydraulic Type |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |