| About |
|---|
| Product Description | |
|---|---|
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.385 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 18 | g/10min | ISO 1133 |
| Water content | ≤0.4 | % | ISO 1269 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| Broken BRK, 50 mm/min | 32 | MPa | ISO 527 |
| Elongation at Break | |||
| 50 mm/min | 7 | % | ISO 527 |
| Flexural Strength | |||
| 2 mm/min | 24 | MPa | ISO 178 |
| Flexural Modulus | |||
| 2 mm/min | 2700 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | 12 | KJ/m² | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 165-180 | ℃ | ISO 11357-3 |
| Hot deformation temperature HDT | |||
| 0.45 MPa, unannealed | 51 | ℃ | ISO 75-1/-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Time | 4.8 | hr | |
| Drying Temperature | 55-70 | ℃ | |
| Dew point of air | -40 | ℃ | |
| Air flow rate | >1.85 | m3/h/kg | |
| Back Pressure | <1.5 | MPa | |
| Hopper Temperature | 40-60 | ℃ | |
| Front Temperature Zone 3 | 100-140 | ℃ | |
| Middle Temperature Zone 2 | 150-170 | ℃ | |
| Rear Temperature Zone 1 | 160-180 | ℃ | |
| Nozzle temperature | 170-190 | ℃ | |
| Mold Temperature | <15 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |