| About |
|---|
| The MC-170 A/B system is a production oriented fast gel and fast de-mold system. It features a mix ratio and working time ideal for machine dispensing and rapid part mold cycling, for production applications.&& |
| Product Description | |
|---|---|
| Generic | TSU |
| Material Status | Commercial: Active |
| Features | High impact resistance,Sprayable |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：12.7 mm | 0.60 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 71.1 | ℃ | ASTM D648 |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| 25℃ | 740 | cP | ASTM D2393 |
| stripping time | |||
| 25℃ | 30 to 60 | min | |
| Post curing time | |||
| 52℃ | 2.0 to 4.0 | hr |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 70 | ASTM D2240 | |
| Tensile modulus | 586 | MPa | ASTM D638 |
| tensile strength | 23.9 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 35 | % | ASTM D638 |
| Bending modulus | 416 | MPa | ASTM D790 |
| bending strength | 14.5 | MPa | ASTM D790 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |