| About |
|---|
| Non-halogen flame retardant compound Macromeric ® 0103-212bBK is a black, UV resistant, non-halogen flame retardant RoHS polyolefin compound. It is designed for use in a wide variety of jacketing applications including wire and cable and tube bundles. This compound has superior fire performance; including slow flame propagation, self-extinguishing characteristics, and low smoke production. Macromeric ® 0103-212bBK should be extruded with a screw configuration designed to optimize process conditions and throughput.&& |
| Product Description | |
|---|---|
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low smoke,Halogen free,Flame Characteristics,Self-extinguishing |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 16 | g/10min | ASTM D1238 |
| Ash Content | |||
| Procedure B | 44 | % | ASTM D5630 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | |||
| 23℃ | 56.0 | kN/m | ASTM D470 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 121℃，168 hr | 5.0 | % | ASTM D638 |
| The rate of change in ultimate elongation in air | |||
| 121℃，168 hr | -15 | % | ASTM D638 |
| The rate of change in tensile strength | |||
| 70℃，4 hr，in Oil | -15 | % | ASTM D638 |
| Change rate of ultimate elongation | |||
| 70 ℃, 4 hours in oil | -5.0 | % | ASTM D638 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -35.0 | ℃ | ASTM D746 |
| UL temperature rating | 90 | ℃ | UL 1581 |
| deformation | |||
| 2000gram load，100℃ | 5.0 | % | UL 1277 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 35 | % | ASTM D2863 |
| Smoke density | ASTM E662 | ||
| Flaming Mode | 30 | Ds | ASTM E662 |
| Smoldering Mode | 230 | Ds | ASTM E662 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 1 second | 95 | ASTM D2240 | |
| tensile strength | |||
| fracture | 13.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 200 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 186 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60 | °C | |
| Drying time | 6.0 to 8.0 | hr | |
| Barrel 1 zone temperature | 149 to 160 | °C | |
| Barrel 2 zone temperature | 166 to 177 | °C | |
| Barrel 3 zone temperature | 177 to 188 | °C | |
| Barrel 4 zone temperature | 177 to 188 | °C | |
| Melt temperature | 182 to 193 | °C | |
| Head temperature | 171 to 182 | °C | |
| Nozzle temperature | 188 to 199 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |