| Overview: MAGNUM 342EZ is a standard heat ABS. It is a reliable and cost effective solution for general covered interior automotive applications. MAGNUM 342EZ has high flow characteristics supporting part design freedom. Benefits: Lot to lot consistency allowing for optimal machine parameters settings from the start Low VOC allowing a better interior air quality facing increasing regulatory and OEMs constraints. Heat stability during wide range of processing temperatures: enhanced part design freedom Applications: General purpose covered interior automotive applications Mid-consoles Door liners Seat trims&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,Low Gloss |
| Availabilitys | North America,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Density | 1.05 | g/cm³ | ISO 1183-2 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 6.0 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 220℃，10 kg | 22.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1800 | MPa | ISO 527-2 2 |
| 3.20 mm, injection molded | 1790 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 3.20 mm, injection molding | 41.4 | MPa | ASTM D638 |
| yield | 37.0 | MPa | ISO 527-2 2 |
| Tensile strain | |||
| Yield, 3.20 mm, injection molding | 3.0 | % | ASTM D638 |
| yield | 2.3 | % | ISO 527-2 2 |
| Nominal strain at break | > 50 | % | ISO 527-2 2 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2000 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 58.6 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 16.0 | kJ/m² | ISO 179/1eA 2 |
| -30℃ | 8.00 | kJ/m² | ISO 179/1eA 2 |
| Charpy impact strength | |||
| 23℃ | No Break | ISO 179/1eU 2 | |
| -30℃ | No Break | ISO 179/1eU 2 | |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -18 ℃, 3.2mm, injection molding | 80 | J/m | ASTM D256 |
| 23 ℃, 3.2mm, injection molding | 160 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| 23 ℃, 3.20 mm, injection molded, Peak Energy | 32.8 | J | ASTM D3763 |
| 23 ℃, 3.20 mm, injection molding, Total Energy | 42.9 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 76.7 | ℃ | ASTM D648 |
| 1.8 MPa | 80.0 | ℃ | ISO 75-2 2 |
| 0.45 MPa, unannealed | 90.6 | ℃ | ASTM D648 |
| 0.45 MPa | 89.0 | ℃ | ISO 75-2 2 |
| Vicat Softening Temp | 104 | ℃ | ASTM D1525 5 |
| B50 | 94.0 | ℃ | ISO 306 2 |
| Linear coefficient of thermal expansion | |||
| MD | 7.8E-5 | 1/℃ | ISO 11359-2 2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 to 85 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Processing (melt) temperature | 232 to 246 | °C | |
| Mold temperature | 27 to 49 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Clamping force | 2.8 to 4.1 | kN/cm² | |
| Screw length to diameter ratio | 20.0:1.0 | ||
| Screw compression ratio | 1.5:1.0 to 3.5:1.0 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |