| About |
|---|
| MAGNUM* 3504 is a general purpose resin and can be used for both injection moulding and extrusion applications. This grade combines high impact with medium-high heat resistance. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring. Applications: General purpose extrusion and injection moulding applications&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,High Heat Resistance,HB |
| Availabilitys | Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183/B |
| Apparent density | 0.65 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 5.2 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 220℃，10 kg | 5.30 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 3.20 mm, injection molded | 2140 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 3.20 mm, injection molding | 43.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 3.20 mm, injection molding | 2.7 | % | ISO 527-2/50 |
| Bending modulus | |||
| 3.20 mm, injection molded | 2050 | MPa | ISO 178 |
| bending strength | |||
| 3.20 mm, injection molded | 65.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30 ℃, injection molding | 13 | kJ/m² | ISO 179/1eA |
| -30 ℃, injection molding | 9.0 | kJ/m² | ISO 179/2C |
| 23 ℃, injection molding | 23 | kJ/m² | ISO 179/1eA |
| 23 ℃, injection molding | 15 | kJ/m² | ISO 179/2C |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30 ℃, injection molding | 12 | kJ/m² | ISO 180-1A |
| 23 ℃, injection molding | 25 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 101 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 102 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 2.0 mm | 55 | mm/min | ISO 3795 |
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| carbon emission | 30.0 | µg/g | VDA 277 |
| atomization | 98 | % | ISO 6452 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 3-points |
| 4. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |