| About |
|---|
| MAGNUM* 3513 is a grade which combines high impact with good flowability. It is suitable for injection moulding and extrusion applications. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring. Applications: Extruded sheet Profiles General injection moulding&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Good liquidity |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.55 | % | ISO 294-4 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 8.60 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 47.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.3 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 2360 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 70.0 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 2200 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 100 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 101 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 8.0E-5 | 1/℃ | ISO 11359-2 |
| TD | 6.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | > 1.0E+13 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 2.70 | KV/mm | IEC 60243-1 | |
| Dielectric constant | |||
| 23℃ | 8.0E-3 | 1 MHz | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75mm | UL 94 | ||
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 24 | kJ/m² | ISO 179/1eA |
| -30℃ | 11 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 23 | kJ/m² | ISO 180-1A |
| -30℃ | 11 | kJ/m² | ISO 180-1A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 85.0 | °C | |
| Drying time | 3.0-4.0 | Hr | |
| Injection temperature | |||
| Rear barrel temperature | 180-190 | °C | |
| Central temperature of the barrel | 190-220 | °C | |
| Barrel front temperature | 190-220 | °C | |
| Die temperature | 200-230 | °C | |
| Mold temperature | 60-80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3. 0.079 in/min |
| 4. 3-points |
| 5. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |