| About |
|---|
| High Heat, Low Gloss, Medium Impact ABS resin for injection molding Applications: Automotive interior trim applications requiring low volatile organic compounds (VOC).&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,Low odor,Low Gloss |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ASTM D792 |
| Density | 1.06 | g/cm³ | ISO 1183/B |
| Melt Flow Rate | |||
| 230℃，3.80kg | 2.1 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| TD | 0.56 | % | ASTM D955 |
| MD | 0.57 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2300 | MPa | ASTM D638 |
| Tensile modulus | 2330 | MPa | ISO 527-2/50 |
| tensile strength | |||
| yield | 47.0 | MPa | ISO 527-2/50 |
| yield | 49.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.5 | % | ISO 527-2/50 |
| fracture | 8.8 | % | ASTM D638 |
| yield | 2.9 | % | ISO 527-2/50 |
| yield | 3.1 | % | ASTM D638 |
| Bending modulus | 2410 | MPa | ASTM D790 |
| Bending modulus | 2300 | MPa | ISO 178 |
| bending strength | 76.5 | MPa | ASTM D790 |
| bending strength | 71.7 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 11 | kJ/m² | ISO 179/1eA |
| 23℃ | 22 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 130 | J/m | ASTM D256 |
| 23℃ | 220 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 10 | kJ/m² | ISO 180-A |
| 23℃ | 16 | kJ/m² | ISO 180-A |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Peak Energy | 23.0 | J | ASTM D3763 |
| 23℃，Peak Energy | 30.1 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 84.0 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 81.7 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 99.4 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 98.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 105 | ℃ | ASTM D1525 6 |
| B50 | 105 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| TD：-40~100℃ | 9.5E-5 | 1/℃ | ASTM E831 |
| MD：-40~100℃ | 7.7E-5 | 1/℃ | ASTM E831 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| FMVSS Flammability | 30 | mm/min | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 to 85 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 238 | °C | |
| Barrel middle temperature | 249 | °C | |
| Barrel front temperature | 254 | °C | |
| Nozzle temperature | 249 to 254 | °C | |
| Processing (melt) temperature | 243 to 271 | °C | |
| Mold temperature | 38 to 66 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Method I (3 point load), 0.079 in/min |
| 4. 0.079 in/min |
| 5. 3-points |
| 6. Rate A (50°C/h), Loading 2 (50 N) |
| 7. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |