| About |
|---|
| Overview: MAGNUM™ 3904 is a medium heat ABS. Its very high impact properties make it suitable for main interior automotive applications. MAGNUM™ 3904 is available in Europe and China, locally produced in major car production regions. Due to its excellent extrusion capabilities, this product is also used for large thermoformed parts, for Truck and Bus applications. Benefits: Lot to lot consistency allowing for optimal machine parameters settings from the start Self-coloring enabling improvement of costs by using less pigments and lowering your logistic costs Low VOC allowing a better interior air quality facing increasing regulatory and OEMs constraints. Heat stability during wide range of processing temperatures: enhanced part design freedom Contains low amounts of gels providing for excellent thermoformability with low levels of scrap Applications: Main interior automotive applications requiring high impact Various interior trims, under the beltline Large sized applications in commercial transportation Complies with: U.S. FDA FCN 1525&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183/B |
| Density | 1.05 | g/cm³ | ISO 1183-2 |
| Apparent density | 0.65 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 4.5 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 220℃，10 kg | 4.70 | cm³/10min | ISO 1133 |
| 220℃，10 kg | 4.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1900 | MPa | ISO 527-2 2 |
| 3.20 mm, injection molded | 1820 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 35.0 | MPa | ISO 527-2 2 |
| Yield, 3.20 mm, injection molding | 37.0 | MPa | ISO 527-2/50 |
| Yield, 3.20 mm, injection molding | 39.0 | MPa | ISO 527-2/100 |
| Tensile strain | |||
| yield | 2.5 | % | ISO 527-2 2 |
| Yield, 3.20 mm, injection molding | 2.6 | % | ISO 527-2/50 |
| Yield, 3.20 mm, injection molding | 2.8 | % | ISO 527-2/100 |
| Nominal strain at break | 45 | % | ISO 527-2 2 |
| Bending modulus | |||
| 3.20 mm, injection molded | 1900 | MPa | ISO 178 |
| bending strength | |||
| 3.20 mm, injection molded | 58.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 38.0 | kJ/m² | ISO 179/1eA 2 |
| -30℃ | 16.0 | kJ/m² | ISO 179/1eA 2 |
| -30 ℃, injection molding | 12 | kJ/m² | ISO 179/2C |
| -30 ℃, injection molding | 18 | kJ/m² | ISO 179/1eA |
| 23 ℃, injection molding | 37 | kJ/m² | ISO 179/1eA |
| 23 ℃, injection molding | 22 | kJ/m² | ISO 179/2C |
| Charpy impact strength | |||
| 23℃ | No Break | ISO 179/1eU 2 | |
| -30℃ | No Break | ISO 179/1eU 2 | |
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30 ℃, injection molding | 17 | kJ/m² | ISO 180-A |
| 23 ℃, injection molding | 42 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 97.0 | ℃ | ISO 75-2/A |
| 1.8 MPa | 97.0 | ℃ | ISO 75-2 2 |
| Vicat Softening Temp | |||
| B50 | 97.0 | ℃ | ISO 306 |
| B50 | 97.0 | ℃ | ISO 306 2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+13 | ohms·m | IEC 60093 2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 2.0 mm | 40 | mm/min | ISO 3795 |
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Flame retardant level | |||
| 1.60 mm | HB | ISO 1210 2 | |
| carbon emission | 20.0 | µg/g | VDA 277 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3. 0.079 in/min |
| 4. 3-points |
| 5. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |