| MAGNUM™ 555 ABS resin is low gloss, low flow ABS resin that has a sheet Izod impact strength of 6.6 ft-lb/in. MAGNUM ABS resins are thermoplastic materials that provide an excellent balance of processability, impact resistance, and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resins are available in a wide range of melt flow rates, impact strengths, and heat resistances for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion, and thermoforming. The sheet and thermoforming grades of MAGNUM ABS resins provide excellent high and low gloss aesthetics, good thermal color stability, heat and impact resistance, and stiffness. MAGNUM ABS resins can fill a variety of needs by offering ranges in melt flow rates from 1.0 to 4.0, sheet Izod impacts from 2.5 to 10.5 ft-lb/in and sheet flexural modulus from 285,000 to 300,000 psi. Applications Burial vault liners Tool cases Recreational vehicles Luggage Signs Complies with: U.S. FDA 21 CFR 181.32 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good surface appearance,Low liquidity,High impact resistance,Good color stability,High Heat Resistance,Low Gloss,HB |
| Availabilitys | North America |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Density | 1.05 | g/cm³ | ISO 1183-2 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 2.4 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 220℃，10 kg | 9.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2340 | MPa | ASTM D638 |
| Tensile modulus | 2200 | MPa | ISO 527-2 2 |
| tensile strength | |||
| fracture | 35.2 | MPa | ASTM D638 |
| yield | 47.0 | MPa | ISO 527-2 2 |
| yield | 43.4 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 2.6 | % | ISO 527-2 2 |
| Nominal strain at break | 20 | % | ISO 527-2 2 |
| Bending modulus | 2550 | MPa | ASTM D790 |
| bending strength | 77.9 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 40.0 | kJ/m² | ISO 179/1eA 2 |
| -30℃ | 12.0 | kJ/m² | ISO 179/1eA 2 |
| Charpy impact strength | |||
| 23℃ | No Break | ISO 179/1eU 2 | |
| -30℃ | No Break | ISO 179/1eU 2 | |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -18℃，3.2mm | 140 | J/m | ASTM D256 |
| 23℃，3.2mm | 430 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa | 82.0 | ℃ | ISO 75-2 2 |
| 0.45 MPa | 95.0 | ℃ | ISO 75-2 2 |
| Vicat Softening Temp | 108 | ℃ | ASTM D1525 |
| B50 | 98.0 | ℃ | ISO 306 2 |
| Linear coefficient of thermal expansion | |||
| MD | 7.9E-5 | 1/℃ | ISO 11359-2 2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 100 Hz | 2.79 | ASTM D150 | |
| Dissipation factor | |||
| 100 Hz | 4.0E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Flame retardant level | |||
| 1.60 mm | HB | ISO 1210 2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 85 | ASTM D523 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 to 88 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Processing (melt) temperature | 218 to 274 | °C | |
| Mold temperature | 27 to 60 | °C | |
| Back pressure | 0.345 to 3.45 | MPa | |
| Clamping force | 2.8 to 6.9 | kN/cm² | |
| Screw length to diameter ratio | 20.0:1.0 | ||
| Screw compression ratio | 1.5:1.0 to 3.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3. Type I, 2.0 in/min |
| 4. Type I, 0.050 in/min |
| 5. 10 mil Notch Depth |
| 6. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |