| About |
|---|
| MAJORIS AG100E is a 10% glass fibre reinforced polyethylene high density compound intended for injection moulding and extrusion profiles. The product is available in black (MAJORIS AG100E – 8229) and natural (MAJORIS AG100E) but other colours can be provided on request. APPLICATIONS MAJORIS AG100E is intended for components which require good impact strength, rigidity, dimensional stability. Suitable applications are: Electrical tool and appliance components Miscellaneous automotive technical items Profile&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good Dimensional Stability,Renewable resources,High density,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 0.20 | g/10min | ISO 1133 |
| 190℃，21.6kg | 18 | g/10min | ISO 1133 |
| 190℃，5.0kg | 0.60 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：2.0 mm | 0.90 | % | |
| MD：2.0 mm | 1.1 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 30.0 | MPa | ISO 527-2/50 |
| Bending modulus | 1490 | MPa | ISO 178 |
| bending strength | 47.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 17 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 70 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 65.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 106 | ℃ | ISO 75-2/B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 200 to 220 | °C | |
| Processing (melt) temperature | 210 to 250 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Injection speed | Moderate | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 2.0 in/min |
| 4. at Yield |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |