| About |
|---|
| AN081 is a polypropylene copolymer for injection moulding, extrusion and blow moulding. APPLICATIONS AN081 is recommended for applications like: Heater housings Break fluid reservoirs&& |
| Product Description | |
|---|---|
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Renewable resources,Copolymer,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.30 | g/10min | ISO 1133 |
| Shrinkage rate | 1.9 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 3.8 | kJ/m² | ISO 179/1eA |
| -20℃ | 4.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 60 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20℃ | No Break | ISO 179/1eU | |
| 23℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -20℃ | 5.5 | kJ/m² | ISO 180-1A |
| 23℃ | 55 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 50.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 80.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| — | 151 | ℃ | ISO 306/A |
| — | 70.0 | ℃ | ISO 306/B |
| Linear coefficient of thermal expansion | |||
| MD：-30~80℃ | 8.2E-5 | 1/℃ | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1150 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 27.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | > 300 | % | ISO 527-2/50 |
| yield | 11 | % | ISO 527-2/50 |
| Bending modulus | 1350 | MPa | ISO 178 |
| bending strength | 35.0 | MPa | ISO 178 |
| Ball hardness | |||
| H 132/10 | 48.0 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 40 to 80 | °C | |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Hold pressure | 30.0 to 60.0 | MPa | |
| Injection Velocity | 100 to 200 | mm/sec | |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Barrel 1 zone temperature | 210 to 250 | °C | |
| Barrel 3 zone temperature | 210 to 250 | °C | |
| Barrel 5 zone temperature | 210 to 250 | °C | |
| Melt temperature | 220 to 260 | °C | |
| Head temperature | 220 to 260 | °C | |
| Nozzle temperature | 220 to 260 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |