AT368 – 9411 is a filled talc reinforced, high molecular weight, low melt index flow rate polypropylene block copolymer with a very high stiffness at a good level of impact strength and UV stabilised. APPLICATIONS AT368 – 9411 is recommended for the extrusion of profiles (building, electrical, furniture and construction profiles or pipes). Products made from this material show a high dimensional stability and low process shrinkage.&&

About

AT368 – 9411 is a filled talc reinforced, high molecular weight, low melt index flow rate polypropylene block copolymer with a very high stiffness at a good level of impact strength and UV stabilised. APPLICATIONS AT368 – 9411 is recommended for the extrusion of profiles (building, electrical, furniture and construction profiles or pipes). Products made from this material show a high dimensional stability and low process shrinkage.&&

Product Description
Generic	PP copolymer
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,Low liquidity,High impact resistance,Good Dimensional Stability,Renewable resources,Low contractility,Block Copolymer,High molecular weight,HB
Availabilitys	Europe
Process Methods	Profile extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.14	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	0.60	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	3160	MPa	ISO 527-1-2
tensile strength
yield	30.5	MPa	ISO 527-2/50
Tensile strain
yield	4.0	%	ISO 527-2/50

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-20℃	2.0	kJ/m²	ISO 179/1eA
23℃	9.0	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	76.0	℃	ISO 306/B

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

Process Conditions
Extrusion	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	3.0	hr
Barrel 1 zone temperature	190 to 230	°C
Barrel 3 zone temperature	190 to 230	°C
Barrel 5 zone temperature	190 to 230	°C
Melt temperature	200 to 230	°C
Head temperature	200 to 230	°C
Nozzle temperature	200 to 230	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.