| About |
|---|
| EE081 is a elastomer modified polypropylene compound intended for injection moulding. The product is available in black (EE081 – 8229) and natural (EE081) but other colours can be provided on request. EE081 has a very easy flowing and very good process ability. APPLICATIONS Injection moulded parts.&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Renewable resources,Good liquidity,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| 2.0 mm | 1.3 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 69 | ISO 868 | |
| Tensile modulus | 950 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 21.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.0 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 51.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 75.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 141 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 230 to 260 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Injection speed | Slow-Moderate | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |