| About |
|---|
| EE165 – 1791 is a 15% mineral filled polypropylene elastomer modified compound intended for injection moulding. EE165 – 1791 has been developed especially for the automotive interior parts, requiring good impact strength/stiffness, very good scratch resistance and UV resistance. The product is available in natural (EE165) and black (EE165-8229) but other colours can be provided on request. APPLICATIONS Automotive interior parts&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,High impact resistance,Renewable resources,High scratch resistance,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ISO 1133 |
| Shrinkage rate | 0.90 to 1.2 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1750 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 20.0 | MPa | ISO 527-2/50 |
| Bending modulus | 1600 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| 0℃ | 6.0 | kJ/m² | ISO 179/1A |
| 23℃ | 25 | kJ/m² | ISO 179/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 53.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 94.0 | ℃ | ISO 75-2/B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 | hr | |
| Processing (melt) temperature | 220 to 260 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Injection speed | Moderate | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |