| About |
|---|
| FFR057 – 3717 is part of a new material family with low halogen no blooming flame retardant, high impact strength, high gloss and antistatic as well as an excellent UV-resistance and very low war page behaviour. Intended for injection moulding. The product is available in natural (FFR057) but other colours can be provided on request. APPLICATIONS FFR057 – 3717 is recommended for indoor or outdoor electrical and lighting applications like plugs, sockets, connectors, capacitor housings, small junction boxes or lamp covers; where chemical resistance, impact and flammability behaviours are required.&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low warping,Low Halogen Content,Good surface appearance,High impact resistance,Renewable resources,Low to No Fogging,Flame Characteristics,Solvent resistance,Antistatic property,V-2 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.965 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 18 | g/10min | ISO 1133 |
| Spiral flow length | 102 | cm | |
| Shrinkage rate | |||
| TD | 1.2 | % | |
| MD：2.0 mm | 1.2 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1500 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 12.0 | MPa | ISO 527-2 |
| yield | 28.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 80 | % | ISO 527-2 |
| yield | 6.0 | % | ISO 527-2/50 |
| Bending modulus | 1400 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20℃ | 2.2 | kJ/m² | ISO 179/1eA |
| 23℃ | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20℃ | 71 | kJ/m² | ISO 179/1eU |
| 23℃ | 190 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 94.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| — | 154 | ℃ | ISO 306/A |
| — | 79.0 | ℃ | ISO 306/B |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60335-1 | |
| Relative temperature index | |||
| Electrical performance | 110 | ℃ | UL 746 |
| Strength mechanical performance | 115 | ℃ | UL 746 |
| Impact mechanical performance | 115 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 7.8E+15 | ohms | IEC 60093 |
| Volume resistivity | 2.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | 41 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 50 Hz | 2.25 | IEC 60250 | |
| 1 kHz | 2.25 | IEC 60250 | |
| 100 kHz | 2.24 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 50 Hz | 1.5E-3 | IEC 60250 | |
| 1 kHz | 1.5E-3 | IEC 60250 | |
| 100 kHz | 2.0E-3 | IEC 60250 | |
| Arc resistance | |||
| 3.0 mm | PLC 5 | ASTM D495 | |
| Compared to the resistance to leakage and marking index | |||
| 3.00 mm | PLC 0 | UL 746 | |
| Compared to the leakage tracing index | IEC 60112 | ||
| CTI | > 600 | V | IEC 60112 |
| Solution B | > 600 | V | IEC 60112 |
| Needle flame test | |||
| 1.00 mm | Pass | IEC 60695-11-5 | |
| High Arc Burning Index (HAI) | UL 746 | ||
| 1.5 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | UL 746 | ||
| 1.50 mm | PLC 0 | UL 746 | |
| 3.00 mm | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 1.5 mm | PLC 3 | UL 746 | |
| 3.0 mm | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.50 mm, all colors | V-2 | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.50 mm | 850 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1 mm | 850 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 25 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 180 to 200 | °C | |
| Mold temperature | 20 to 50 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Melt Temperature: 392°F |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |