| About |
|---|
| Mapex AN0511 SN PA6 is a 25 % glass fiber / mineral reinforced product for injection moulding in natural colour&& |
| Product Description | |
|---|---|
| Supplier | Ginar Technology |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good surface appearance,Good Electrical Properties,High Heat Resistance,Good wear resistance,Grease resistance,Solvent resistance,Fuel resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ASTM D792 , ISO 1183 |
| Shrinkage rate | |||
| MD：1.6 mm | 0.50 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 76.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.5 | % | ISO 527-2 |
| Bending modulus | 6550 | MPa | ISO 178 |
| bending strength | 145 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 180 | ℃ | ASTM D648，ISO 75-2/A |
| Melting temperature | 220 | ℃ | DSC |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | 150 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 240 to 270 | °C | |
| Barrel middle temperature | 240 to 270 | °C | |
| Barrel front temperature | 240 to 270 | °C | |
| Nozzle temperature | 240 to 250 | °C | |
| Mold temperature | 30 to 100 | °C | |
| Injection pressure | 50.0 to 120 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |