| A superior heat resistant material. U.L. RTI rating of 160°C-170°C&& |
| Product Description | |
|---|---|
| Generic | 热塑性聚酯 |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,V-0 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.75 to 1.80 | g/cm³ | ASTM D792 |
| Shrinkage rate | 2.0 | ASTM D1895 | |
| Shrinkage rate | |||
| MD | 0.050 to 0.20 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.12 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 430 to 530 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | > 260 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | > 14 | kV/mm | ASTM D149 |
| Arc resistance | > 185 | sec | ASTM D495 |
| Inclined（Plane Tracking） | > 1000 | min | ASTM D2303 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Babbitt hardness | 35 to 45 | ASTM D2583 | |
| tensile strength | 41.4 to 55.2 | MPa | ASTM D638 |
| Bending modulus | 11000 to 12400 | MPa | ASTM D790 |
| bending strength | 117 to 131 | MPa | ASTM D790 |
| Compression modulus | 317000 to 345000 | MPa | ASTM D695 |
| compressive strength | 89.6 to 103 | MPa | ASTM D695 |
| shear strength | 48.3 to 55.2 | MPa | ASTM D732 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |