| MARCOBLEND MD7100 is an ignition resistant and glass fiber reinforced polycarbonate ABS resin. The resin is Halogen free and compliance with TCO and RoHS certification. The unique characters include superior processability, good stiffness, and excellent dimension stability and suitable for use in TFT LCD frame and internal structure parts.&& |
| Product Description | |
|---|---|
| Supplier | POLY GIN |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good Dimensional Stability,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 300℃，1.20kg | 26 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.20 to 0.30 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 79.0 | MPa | ASTM D638 |
| Bending modulus | 3720 | MPa | ASTM D790 |
| bending strength | 124 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 72 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 93.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 230 to 245 | °C | |
| Barrel middle temperature | 240 to 255 | °C | |
| Barrel front temperature | 245 to 265 | °C | |
| Nozzle temperature | 250 to 270 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |