| About |
|---|
| This low density polyethylene is tailored for blown film applications that require: Superior strength Good abrasion and tear resistance Exceptional shrink and shrink tension High coefficient of friction Typical blown film applications include: Heavy duty packaging Pallet shrink Case shrink wrap C&A film and container liners&& |
| Product Description | |
|---|---|
| Supplier | Chevron Phillips |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High Friction,High anti-blocking,Good tear strength,Good wear resistance,High shrinkage |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.50 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Blown film | 0.48 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 51 | µm | |
| Oxygen transfer rate | |||
| 51 µ m, blow molded film | 3300 | cm³/m²/24 hr | ASTM D3985 |
| Water vapor transmittance | |||
| 51 µ m, blow molded film | 10 | g/m²/24 hr | ASTM F1249 |
| Drop hammer impact | |||
| 50.8 µ m, blow molded film | 65.6 | kN/m | ASTM D1709 |
| tear strength | ASTM D1922 | ||
| MD，50.8 µm | 54.1 | kN/m | ASTM D1922 |
| TD，50.8 µm | 50.2 | kN/m | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 99.0 | ℃ | ASTM D1525 |
| Melting temperature | 111 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, 50.8 µ m, blow molded film | 89 | ASTM D2457 | |
| Haze | |||
| 50.8 µ m, blow molded film | 11 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |