About |
---|
This linear low density polyethylene is an ethylene-hexene copolymer tailored for blown film applications that require: Good toughness properties Increased stiffness Low creep Good drawdown Excellent processing characteristics Use alone or in coextrusions; blends with other polyolefins Typical blown film applications include: Industrial films and bags that require added stiffness Thin gauge applications General purpose packaging&& |
Product Description | |
---|---|
Supplier | Chevron Phillips |
Generic | Linear low density polyethylene |
Material Status | Commercial: Active |
Features | Good Rigidity,Excellent Processability,Good flexibility,Smoothness,Good dissection,Low anti-blocking,Hexene copolymers |
Availabilitys | North America,Latin America |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 0.925 | g/cm³ | ASTM D1505 |
Melt Flow Rate | |||
190℃,2.16kg | 0.80 | g/10min | ASTM D1238 |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
friction coefficient | |||
Blown film | 0.15 | ASTM D1894 |
film | Nominal value | Unit | Test method |
---|---|---|---|
Secant modulus | ASTM D882 | ||
1% secant, MD: 25 µ m, blow molded film | 290 | MPa | |
1% secant, TD: 25 µ m, blow molded film | 345 | MPa | |
tensile strength | ASTM D882 | ||
MD, fracture, 25 µ m, blow molded film | 55.0 | MPa | |
TD, fracture, 25 µ m, blow molded film | 34.0 | MPa | |
Tensile strain | ASTM D882 | ||
MD, fracture, 25 µ m, blow molded film | 400 | % | |
TD, fracture, 25 µ m, blow molded film | 700 | % | |
Drop hammer impact | |||
25.4 µ m, blow molded film | 48.3 | kN/m | ASTM D1709 |
tear strength | ASTM D1922 | ||
MD,25.4 µm | 115.8 | kN/m | |
TD,25.4 µm | 251.0 | kN/m |
optical performance | Nominal value | Unit | Test method |
---|---|---|---|
gloss | |||
60 °, 25.4 µ m, blow molded film | 65 | ASTM D2457 | |
Haze | |||
25.4 µ m, blow molded film | 18 | % | ASTM D1003 |
Notes |
---|
1. Typical properties: these are not to be construed as specifications. |
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |