| MarFlex® HHM TR-257是一种线性低密度聚乙烯材料,。 该产品在北美洲或拉丁美洲有供货,加工方式为:吹塑薄膜或共挤出成型。 MarFlex® HHM TR-257的主要特性有: 高收缩性 加工性能良好 加工助剂 典型应用领域包括: 包袋/内衬 包装&& |
| Product Description | |
|---|---|
| Supplier | Chevron Phillips |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good dissection,Good melt strength,Good thermal contraction,High shrinkage |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.20 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | 0.35 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| 1% secant, MD | 365 | MPa | |
| 1% secant, TD | 503 | MPa | |
| tensile strength | ASTM D882 | ||
| MD, fracture | 72.4 | MPa | |
| TD, fracture | 29.6 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 380 | % | |
| TD, fracture | 800 | % | |
| Drop hammer impact | |||
| 25 µm | 46 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：25 µm | 12 | g | |
| TD：25 µm | 950 | g |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 46 | ASTM D2457 | |
| Haze | 33 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |