| About |
|---|
| This autoclave LDPE homopolymer is tailored for applications that require: Excellent flexibility Excellent flow Good warpage resistance Typical injection molded applications for 1003 include: Housewares Tamper evident, snap-on caps Wine bottle sleeve caps This resin meets these specifications: ASTM D4976 – PE 112 FDA 21 CFR 177.1520(c) 2.2, use conditions B through H per 21 CFR 176.170(c)&& |
| Product Description | |
|---|---|
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Low warping,Good flexibility,Good liquidity,Food contact compliance,High pressure heat resistance,Homopolymer |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.917 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 13 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 46 | ASTM D2240 | |
| tensile strength | |||
| Yield, molding | 9.00 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 550 | % | ASTM D638 |
| Bending modulus | |||
| Tangent, molded | 200 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -52.0 | ℃ | ASTM D746A |
| Vicat Softening Temp | 86.0 | ℃ | ASTM D1525 4 |
| Notes |
|---|
| 1. use conditions B through H |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. Type IV, 2.0 in/min |
| 4. 0.50 in/min |
| 5. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |