| This linear low density polyethylene is an ethylene-hexene copolymer tailored for film applications that require: Excellent processing characteristics Exceptional drawdown Use alone or in coextrusions; blends with other polyolefins Good stiffness at thin gauges Available with slip or high stabilization package Typical blown film applications include: Coextrusions Blend component to improve drawdown Thin gauge applications General purpose packaging Typical cast film applications include: Stretch wrap Overwrap Coextrusions Nominal&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Excellent Processability,Good dissection,Hexene copolymers |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| Casting thin film | > 1.0 | ASTM D1894 | |
| Blown film | 0.80 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 25 µ m, blow molded film | 228 | MPa | ASTM D882 |
| 1% secant, MD: 32 µ m, cast thin film | 200 | MPa | ASTM D882 |
| 1% secant, TD: 25 µ m, blow molded film | 276 | MPa | ASTM D882 |
| 1% secant, TD: 32 µ m, cast thin film | 214 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, fracture, 25 µ m, blow molded film | 45.0 | MPa | ASTM D882 |
| MD, fracture, 32 µ m, blow molded film | 43.0 | MPa | ASTM D882 |
| TD, fracture, 25 µ m, blow molded film | 38.0 | MPa | ASTM D882 |
| TD, fracture, 32 µ m, blow molded film | 33.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 25 µ m, blow molded film | 500 | % | ASTM D882 |
| MD, fracture, 32 µ m, extruded film | 580 | % | ASTM D882 |
| TD, fracture, 25 µ m, blow molded film | 750 | % | ASTM D882 |
| TD, fracture, 32 µ m, extruded film | 780 | % | ASTM D882 |
| Drop hammer impact | |||
| 31.8 µ m, cast thin film | 54.1 | kN/m | ASTM D1709 |
| 25 µ m, blow molded film | 180 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 25 µ m, blow molded film | 300 | g | ASTM D1922 |
| TD: 25 µ m, blow molded film | 750 | g | ASTM D1922 |
| tear strength | ASTM D1922 | ||
| MD，31.8 µm | 115.8 | kN/m | ASTM D1922 |
| TD，31.8 µm | 212.3 | kN/m | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D2457 | ||
| 60 °, 1.00 µ m, blow molded film | 65 | ASTM D2457 | |
| 60 °, 31.8 µ m, cast thin film | 140 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 25.4 µ m, blow molded film | 18 | % | ASTM D1003 |
| 31.8 µ m, cast thin film | 3.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |