| This high density polyethylene is an ethylene-hexene copolymer that is tailored for injection molded applications that: Require good flow Require good impact strength Require good stiffness Are durable and recyclable for sustainability Typical injection molded applications for 9018 include: Pails (one- and two-gallon) Automotive applications Toys Tamper-evident caps for milk bottles Small containers for building compounds Housewares This resin meets these specifications: ASTM D4976 – PE 232 FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per 21 CFR 176.170(c)&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Renewable resources,Good liquidity,Food contact compliance,Durability,Hexene copolymers |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 20 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 100% non-ionic detergent, molded, F50 | < 10.0 | hr | ASTM D1693B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 63 | ASTM D2240 | |
| tensile strength | |||
| Yield, molding | 27.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 300 | % | ASTM D638 |
| Bending modulus | |||
| Tangent, molded | 1200 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -75.0 | ℃ | ASTM D746A |
| Vicat Softening Temp | 122 | ℃ | ASTM D1525 4 |
| Notes |
|---|
| 1. use conditions B through H |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. Type IV, 2.0 in/min |
| 4. 0.50 in/min |
| 5. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |