| About |
|---|
| This extra high molecular weight, ethylene-hexene copolymer is tailored for large blow molded and thermoformed parts that require: Good melt strength Good rigidity Excellent ESCR Excellent low temperature impact strength Durability Recyclability Typical blow molded applications for HXM 50100 include: Shipping containers Jerry cans Fuel containers Agricultural chemical tanks Typical thermoformed applications for HXM 50100 include: Pallets Automotive dunnage Truck bedliners Playground equipment This resin meets these specifications: ASTM D4976 – PE 235 FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per Table 2 of 21 CFR 176.170(c) UL94HB yellow card per UL file E54700 NSF Standard 61 for potable water Listed in the Drug Master File&& |
| Product Description | |
|---|---|
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Good melt strength,Ultra high molecular weight,Durability,low-temperature impact resistance,Hexene copolymers,High ESCR,HB |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.948 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 10 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 100% non-ionic detergent, molded, F50 | > 600 | hr | ASTM D1693B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 68 | ASTM D2240 | |
| tensile strength | |||
| Yield, molding | 25.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 700 | % | ASTM D638 |
| Bending modulus | |||
| Tangent, molded | 1200 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile impact strength | |||
| Compression Molding | 190 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, molded | 78.0 | ℃ | ASTM D648 |
| Embrittlement temperature | < -75.0 | ℃ | ASTM D746A |
| Vicat Softening Temp | 126 | ℃ | ASTM D1525 5 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Notes |
|---|
| 1. use conditions B through H |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. Type IV, 2.0 in/min |
| 4. 0.50 in/min |
| 5. Type S |
| 6. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |