| About |
|---|
| Marlex® HXM 50100-01是一种高密度 (HMW) 聚乙烯材料,。 该产品在北美洲或拉丁美洲有供货,加工方式为:吹塑成型、挤出或热成型。 Marlex® HXM 50100-01的主要特性有: 高分子量 高抗环境应力断裂能力 (ESCR) 环保/绿色 己烯共聚单体 坚硬 典型应用领域包括: 罐子 包袋/内衬 工程/工业配件 汽车行业 容器&& |
| Product Description | |
|---|---|
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | Renewable resources,Food contact compliance,Good melt strength,Ultra high molecular weight,Durability,low-temperature impact resistance,Hexene copolymers,High ESCR |
| Availabilitys | North America,Latin America |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.948 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 12 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 100% non-ionic detergent, molded, F50 | > 600 | hr | ASTM D1693B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 66 | ASTM D2240 | |
| tensile strength | |||
| Yield, molding | 25.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, molded | 750 | % | ASTM D638 |
| Bending modulus | |||
| Tangent, molded | 1200 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile impact strength | |||
| Compression Molding | 170 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, molded | 69.0 | ℃ | ASTM D648 |
| Embrittlement temperature | < -75.0 | ℃ | ASTM D746A |
| Vicat Softening Temp | 124 | ℃ | ASTM D1525 5 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |