| About |
|---|
| MARPOL P1902, Polyolefin Plastomer is an ethylene alpha-olefin resin designed for use in a variety of demanding packaging applications including high-speed and form-fill seal packaging. This resin offers excellent ultimate hot tack strength and low temperature seal initiation, even through contamination in the package.&& |
| Product Description | |
|---|---|
| Generic | POP |
| Material Status | Commercial: Negative |
| Features | Thermal viscous strength |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.902 | g/cm³ | ASTM D792 |
| Melt Flow Rate | 1.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| 2% secant, MD | 91.7 | MPa | ASTM D882 |
| 2% secant, TD | 92.4 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield | 7.24 | MPa | ASTM D882 |
| TD, yield | 6.89 | MPa | ASTM D882 |
| MD, fracture | 58.6 | MPa | ASTM D882 |
| TD, fracture | 44.7 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 620 | % | ASTM D882 |
| TD, fracture | 630 | % | ASTM D882 |
| Drop hammer impact | 830 | g | ASTM D1709B |
| Elmandorf tear strength | ASTM D1922 | ||
| MD | 550 | g | ASTM D1922 |
| TD | 720 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 86.1 | ℃ | ASTM D1525 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | 141 | ASTM D2457 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |