| About |
|---|
| Matrixx 665E0 is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in North America. Characteristics include: Flame Rated Impact Resistant&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | High impact resistance,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.8 to 2.4 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 46.2 | MPa | ASTM D638 |
| Bending modulus | |||
| tangent | 1790 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 800 | J/m | ASTM D256 |
| Drop hammer impact | > 36.2 | J | ASTM D5420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative temperature index | |||
| Strength mechanical performance | 65.6 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 to 82 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 249 to 293 | °C | |
| Barrel middle temperature | 249 to 293 | °C | |
| Barrel front temperature | 249 to 293 | °C | |
| Processing (melt) temperature | 271 to 293 | °C | |
| Mold temperature | 52 to 82 | °C | |
| Injection speed | Moderate-Fast | ||
| Back pressure | < 0.345 | MPa | |
| Cushion | 3.18 to 6.35 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |