Matrixx FPP5A30CC

About
Matrixx FPP5A30CC is a Polypropylene product filled with 30% glass fiber. It is available in North America. Characteristics include: Flame Rated Chemically Coupled Impact Resistant&&

Product Description
Generic	PP not specified
Material Status	Commercial: Active
Features	High impact resistance,Chemical coupling,HB
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.13	g/cm³	ASTM D792
Melt Flow Rate
230℃，2.16kg	4.0	g/10min	ASTM D1238
Shrinkage rate
MD：3.2 mm	0.10 to 0.40	%	Internal Method

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	53.8	MPa	ASTM D638
Bending modulus
tangent	3450	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	230	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Relative temperature index	65.6	℃	UL 746

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
1.50 mm	HB		UL 94

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	82 to 104	°C
Drying time	2.0 to 4.0	hr
Barrel rear temperature	199 to 243	°C
Barrel middle temperature	199 to 243	°C
Barrel front temperature	199 to 243	°C
Processing (melt) temperature	199 to 243	°C
Mold temperature	16 to 66	°C
Injection speed	中等
Back pressure	< 0.345	MPa
Screw speed	20 to 60	rpm
Cushion	6.35 to 12.7	mm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.