| About |
|---|
| MAXIMID 7550GVS is a glass fiber 50%-reinforced and flame-retardant MXD6-PA grade. It is suitable for automotive, electrical & electronics, and consumer parts.&& |
| Product Description | |
|---|---|
| Supplier | Korea Engineering |
| Generic | Nylon MXD6 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.82 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：3.0 mm | 0.20 to 0.30 | % | Internal Method |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.13 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 270 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.6 | % | ISO 527-2 |
| Bending modulus | 19300 | MPa | ISO 178 |
| bending strength | 360 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 224 | ℃ | ISO 75-2/A |
| Melting temperature | 238 | ℃ | DSC |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Dry Air Dryer, A | 90 | °C | |
| Dry Air Dryer, B | 120 | °C | |
| Drying time | |||
| Dry Air Dryer, A | 8.0 | hr | |
| Dry Air Dryer, B | 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 250 to 260 | °C | |
| Barrel middle temperature | 260 to 270 | °C | |
| Barrel front temperature | 265 to 275 | °C | |
| Nozzle temperature | 270 to 280 | °C | |
| Mold temperature | 120 to 140 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |