| About |
|---|
| Impact modified, Good heat stability |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 10 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| injection molding | 6000 | MPa | ISO 527-1-2 |
| Tensile strength | 60.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, injection molding | 5.8 | % | ISO 527-2/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, injection molding | 24 | kJ/m² | ISO 180 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 to 85 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Temperature at the rear of the barrel | 200 to 240 | °C | |
| Temperature in the middle of the barrel | 200 to 240 | °C | |
| Front temperature of material barrel | 200 to 240 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |