| About |
|---|
| Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V-0, and 5VA performance ratings. In addition, many compounds in the Maxxam FR portfolio offer elevated Relative Thermal Index (RTI) ratings.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Moderate liquidity,V-2 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.938 | g/cm³ | ASTM D792 |
| Specific volume | 1.08 | cm³/g | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 9.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD: Injection molding | 1.0 to 2.0 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 31.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 120 | % | ASTM D638 |
| Bending modulus | 1380 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 43 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 98.0 | ℃ | ASTM D648 |
| 0.75 mm | 105 | ℃ | UL 746 |
| 1.5 mm | 110 | ℃ | UL 746 |
| 3.0 mm | 110 | ℃ | UL 746 |
| 0.75 mm | 105 | ℃ | UL 746 |
| 1.5 mm | 110 | ℃ | UL 746 |
| 3.0 mm | 110 | ℃ | UL 746 |
| Relative temperature index | UL 746 | ||
| Electrical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 0.75 mm | 105 | ℃ | UL 746 |
| 1.50 mm | 110 | ℃ | UL 746 |
| 3.00 mm | 110 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | 52 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| High Arc Burning Index (HAI) | UL 746 | ||
| 0.75 mm | PLC 0 | UL 746 | |
| 1.5 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 0.75 mm | PLC 3 | UL 746 | |
| 1.5 mm | PLC 2 | UL 746 | |
| 3.0 mm | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm, all colors | V-2 | UL 94 | |
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 38 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 182 to 199 | °C | |
| Barrel middle temperature | 188 to 204 | °C | |
| Barrel front temperature | 199 to 210 | °C | |
| Nozzle temperature | 204 to 218 | °C | |
| Mold temperature | 16 to 49 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure A |
| 3. Type I, 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |