| About |
|---|
| A flame retardant, halogen-free and low smoke, oil resistant compound. Max. operating temperature 125°C.&& |
| Product Description | |
|---|---|
| Generic | 热塑性聚酯 |
| Material Status | Commercial: Active |
| Features | Low smoke,Crosslinked radiation,Halogen free,Flame Characteristics,High Heat Resistance,Grease resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 160℃，21.6kg | 8.0 | g/10min | ISO 1133 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | IEC 811-1-2 | ||
| 155℃，1008 hr | 20 | % | IEC 811-1-2 |
| 165℃，480 hr | 11 | % | IEC 811-1-2 |
| 180℃，144 hr | 5.9 | % | IEC 811-1-2 |
| Changes in tensile stress during fracture in air | IEC 811-1-2 | ||
| 155℃，1008 hr | -21 | % | IEC 811-1-2 |
| 165℃，480 hr | -25 | % | IEC 811-1-2 |
| 180℃，144 hr | -20 | % | IEC 811-1-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| thermosetting | IEC 540 | ||
| Elongation after unloading | 10 | % | IEC 60540 |
| Elongation under load | 25 | % | IEC 60540 |
| Hot press test | |||
| penetration 4h at 140℃ | 8.0 | % | IEC 811-3-1 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | IEC 60093 | ||
| 23℃ | 3.5E+14 | ohms·cm | IEC 60093 |
| 90 ℃ | 6.6E+11 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 30 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 45 | ISO 7619 | |
| tensile strength | IEC 811-1-1 | ||
| — | 11.5 | MPa | IEC 811-1-1 |
| — | 18.0 | MPa | IEC 811-1-1 |
| Tensile strain | IEC 811-1-1 | ||
| fracture | 230 | % | IEC 811-1-1 |
| fracture | 210 | % | IEC 811-1-1 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 140 to 160 | °C | |
| Barrel 2 zone temperature | 150 to 170 | °C | |
| Barrel 3 zone temperature | 170 to 190 | °C | |
| Barrel 4 zone temperature | 175 to 195 | °C | |
| Barrel 5 zone temperature | 180 to 200 | °C | |
| Connector temperature | 180 to 200 | °C | |
| Head temperature | 180 to 200 | °C | |
| Nozzle temperature | 190 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. After crosslinking |
| 3. Before crosslinking |
| 4. at 200°C/15min/0.2 MPa |
| 5. 500V |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |