| About |
|---|
| An e-beam radiation cross-linkable, halogen-free low smoke compound, offering good mechanical and electrical properties.&& |
| Product Description | |
|---|---|
| Generic | 热塑性聚酯 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Low smoke,Good Electrical Properties,Crosslinked radiation,Halogen free,Flame Characteristics,High Heat Resistance,Low temperature toughness,Good wear resistance,Grease resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 150℃，10.0kg | 3.0 | g/10min | ISO 1133 |
| PH value | > 4.7 | IEC 60754-2 | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| thermosetting | IEC 540 | ||
| Elongation under load | 20 | % | IEC 60540 |
| Residual elongation | 10 | % | IEC 60540 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+12 | ohms·cm | Internal Method |
| Conductivity | < 2.00 | µS/mm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 27 | % | ASTM D2863 |
| Halogen Content | 0 | % | IEC 754-1 |
| toxicity | < 3.00 | NES 713 | |
| Flame test | < 15.0 | sec | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermal shrinkage | |||
| 1hr @ 100℃ | < 0.50 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 52 | ISO 7619 | |
| tensile strength | IEC 811-1-1 | ||
| — | > 10.0 | MPa | IEC 811-1-1 |
| — | 15.0 | MPa | IEC 811-1-1 |
| Tensile strain | IEC 811-1-1 | ||
| fracture | > 230 | % | IEC 811-1-1 |
| fracture | 200 | % | IEC 811-1-1 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 120 to 130 | °C | |
| Barrel 2 zone temperature | 130 to 140 | °C | |
| Barrel 3 zone temperature | 130 to 140 | °C | |
| Barrel 4 zone temperature | 140 to 150 | °C | |
| Barrel 5 zone temperature | 150 to 160 | °C | |
| Connector temperature | 150 to 160 | °C | |
| Head temperature | 170 to 180 | °C | |
| Nozzle temperature | 170 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. After crosslinking |
| 3. Before crosslinking |
| 4. at 200°C/15min/0.2 MPa |
| 5. 1h at 70°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |