| About |
|---|
| A high performance radiation cross-linkable compound, offering excellent mechanical and electrical properties&& |
| Product Description | |
|---|---|
| Generic | 热塑性聚酯 |
| Material Status | Commercial: Active |
| Features | Low smoke,Good Electrical Properties,Crosslinked radiation,Flame Characteristics,High Heat Resistance,Good wear resistance,Grease resistance,Halogenated |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 190℃，21.6kg | 0.60 | g/10min | ISO 1133 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | Internal Method | ||
| 150℃，3000 hr | 15 | % | Internal Method |
| 180℃，240 hr | 5.0 | % | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 70.1 | kN/m | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 54 | ISO 7619 | |
| tensile strength | IEC 811-1-1 | ||
| — | > 10.0 | MPa | IEC 811-1-1 |
| — | 20.0 | MPa | IEC 811-1-1 |
| Tensile strain | IEC 811-1-1 | ||
| fracture | > 600 | % | IEC 811-1-1 |
| fracture | 250 | % | IEC 811-1-1 |
| Abrasion | 190 | cm | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 160 to 170 | °C | |
| Barrel 2 zone temperature | 180 to 190 | °C | |
| Barrel 3 zone temperature | 190 to 200 | °C | |
| Barrel 4 zone temperature | 190 to 200 | °C | |
| Barrel 5 zone temperature | 190 to 200 | °C | |
| Connector temperature | 190 to 200 | °C | |
| Head temperature | 190 to 200 | °C | |
| Nozzle temperature | 205 to 215 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. After crosslinking |
| 3. Before crosslinking |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |