| This compounds results in an extremely smooth surface, while still showing an extrudability at high speeds. The high temperature rating makes this compound an ideal choice for the insulation of heat-resistant wires and cables for applications in areas where wires and cables should withstand the high temperatures in small compartments.&& |
| Product Description | |
|---|---|
| Generic | 热塑性聚酯 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Low smoke,Crosslinked radiation,Flame Characteristics,High Heat Resistance,Low temperature toughness,Grease resistance,Halogenated |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 190℃，21.6kg | 3.5 | g/10min | ISO 1133 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| thermosetting | IEC 540 | ||
| Elongation under load | 40 | % | IEC 60540 |
| Residual elongation | < 10 | % | IEC 60540 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 25 | kV/mm | EN 60243-1 |
| Dielectric constant | |||
| 50 Hz | 2.80 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 27 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 43 | ISO 7619 | |
| tensile strength | IEC 811-1-1 | ||
| — | > 8.00 | MPa | IEC 811-1-1 |
| — | > 16.0 | MPa | IEC 811-1-1 |
| Tensile strain | |||
| fracture | > 500 | % | IEC 811-1-1 |
| fracture | > 300 | % | IEC 811-1-1 |
| Fracture, -50 ℃ | > 30 | % | IEC 811-1-4 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 50 | °C | |
| Drying time | 3.0 | hr | |
| Barrel 1 zone temperature | 130 to 140 | °C | |
| Barrel 2 zone temperature | 140 to 150 | °C | |
| Barrel 3 zone temperature | 150 to 160 | °C | |
| Barrel 4 zone temperature | 155 to 165 | °C | |
| Barrel 5 zone temperature | 155 to 165 | °C | |
| Connector temperature | 155 to 165 | °C | |
| Head temperature | 155 to 165 | °C | |
| Nozzle temperature | 160 to 170 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. After crosslinking |
| 3. Before crosslinking |
| 4. at 200°C/15min/0.2 MPa |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |