| About |
|---|
| This compound is an excellent choice for manufacturing insulated hook-up wires in military and aerospace industries (airframe wire) and component conductors for MIL-C-27500 cables&& |
| Product Description | |
|---|---|
| Generic | PVDF |
| Material Status | Commercial: Active |
| Features | Low smoke,Crosslinked radiation,Flame Characteristics,High Heat Resistance,Low temperature toughness,Good wear resistance,Grease resistance,Halogenated,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.75 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 150℃，21.6kg | 12 | g/10min | ISO 1133 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+11 | ohms·cm | ASTM D257 |
| Dielectric strength | > 15 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 | |
| Extreme oxygen index | 42 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 73 | ISO 7619 | |
| tensile strength | IEC 811-1-1 | ||
| — | > 35.0 | MPa | IEC 811-1-1 |
| — | > 30.0 | MPa | IEC 811-1-1 |
| Tensile strain | |||
| fracture | > 130 | % | ASTM D638 |
| fracture | > 300 | % | IEC 811-1-1 |
| fracture | > 150 | % | IEC 811-1-1 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 195 to 205 | °C | |
| Barrel 2 zone temperature | 195 to 205 | °C | |
| Barrel 3 zone temperature | 200 to 210 | °C | |
| Barrel 4 zone temperature | 210 to 220 | °C | |
| Barrel 5 zone temperature | 210 to 220 | °C | |
| Connector temperature | 215 to 225 | °C | |
| Head temperature | 220 to 230 | °C | |
| Nozzle temperature | 220 to 230 | °C | |
| Extruder screw length to diameter ratio L / D | 25.0:1.0 to 30.0:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. After crosslinking |
| 3. Before crosslinking |
| 4. After ageing in air oven 168h at 200°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |