| This compound is made to meet stringent specifications such as the MIL-W-22759 (SAE AS22759), VG 95218 Part 20, 21, 22 and 23, but also other specifications throughout the industry. Applications include commercial wiring in avionics, satellites, aircraft, helicopter, ships, trains, offshore platforms and high performance military and motorsport electronics.&& |
| Product Description | |
|---|---|
| Generic | ETFE |
| Material Status | Commercial: Active |
| Features | Low smoke,Crosslinked radiation,Flame Characteristics,High Heat Resistance,Low temperature toughness,Good wear resistance,Grease resistance,Halogenated |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.70 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 300℃，5.0kg | 15 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| 230℃，6 hrs | 500.0 | µm | |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 75 | kV/mm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 32 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 68 | ASTM D2240 | |
| tensile strength | 45.0 | MPa | IEC 811-1-1 |
| Tensile strain | |||
| fracture | 130 | % | IEC 811-1-1 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 270 to 280 | °C | |
| Barrel 2 zone temperature | 280 to 290 | °C | |
| Barrel 3 zone temperature | 280 to 295 | °C | |
| Barrel 4 zone temperature | 280 to 295 | °C | |
| Barrel 5 zone temperature | 280 to 295 | °C | |
| Connector temperature | 280 to 295 | °C | |
| Head temperature | 280 to 295 | °C | |
| Nozzle temperature | 280 to 295 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. After crosslinking |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |