| About |
|---|
| Halogen-free, low smoke, flexible at low temperatures, highly oil and extra fuel resistant, radiation cross-linkable, flame retardant, max. operating temperature 125°C, compound for power and telecommunication cables for offshore/Shipboard applications.&& |
| Product Description | |
|---|---|
| Generic | 热塑性聚酯 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Low smoke,Crosslinked radiation,Halogen free,Flame Characteristics,High Heat Resistance,Low temperature toughness,Grease resistance,Fuel resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 165℃，21.6kg | 19 | g/10min | ISO 1133 |
| Mooney viscosity | |||
| ML 1+4，160℃ | 26 | MU | DIN 53523 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | IEC 811-1-2 | ||
| 120℃，240 hr | 22 | % | IEC 811-1-2 |
| 150℃，168 hr | 18 | % | IEC 811-1-2 |
| Changes in tensile stress during fracture in air | IEC 811-1-2 | ||
| 120℃，240 hr | -0.50 | % | IEC 811-1-2 |
| 150℃，168 hr | -21 | % | IEC 811-1-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| thermosetting | IEC 540 | ||
| Elongation under load | 15 | % | IEC 60540 |
| Residual elongation | 5.0 | % | IEC 60540 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 28 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 87 | ISO 7619 | |
| tensile strength | IEC 811-1-1 | ||
| — | 4.40 | MPa | IEC 811-1-1 |
| — | 11.1 | MPa | IEC 811-1-1 |
| Tensile strain | |||
| fracture | 400 | % | IEC 811-1-1 |
| fracture | 270 | % | IEC 811-1-1 |
| Fracture, -40 ℃ | 110 | % | ISO 527-2 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 110 to 130 | °C | |
| Barrel 2 zone temperature | 120 to 140 | °C | |
| Barrel 3 zone temperature | 130 to 150 | °C | |
| Barrel 4 zone temperature | 140 to 160 | °C | |
| Barrel 5 zone temperature | 150 to 170 | °C | |
| Connector temperature | 155 to 175 | °C | |
| Head temperature | 165 to 185 | °C | |
| Nozzle temperature | 170 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. After crosslinking |
| 3. Before crosslinking |
| 4. at 200°C/15min/0.2 MPa |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |