| About |
|---|
| Halogen-free, low smoke, thermoplastic, highly flame retardant compound for the sheathing of low and medium voltage cables in General Installation applications.&& |
| Product Description | |
|---|---|
| Generic | 热塑性聚酯 |
| Material Status | Commercial: Active |
| Features | Low smoke,Halogen free,Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.57 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 150℃，21.6kg | 6.0 | g/10min | ISO 1133 |
| Water absorption rate | |||
| 23℃，24hr | 0.070 | % | IEC 811-1-3 |
| 70℃，10days | 1.17 | mg/cm² | IEC 811-1-3 |
| 23℃，24hr | 0.0650 | mg/cm² | ASTM D570 |
| Mooney viscosity | |||
| ML 1+4，140℃ | 35 | MU | DIN 53523 |
| PH value | > 5.3 | IEC 60754-2 | |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | IEC 811-1-2 | ||
| 100℃，240 hr | 13 | % | IEC 811-1-2 |
| 110℃，168 hr | 7.3 | % | IEC 811-1-2 |
| Changes in tensile stress during fracture in air | IEC 811-1-2 | ||
| 100℃，240 hr | -14 | % | IEC 811-1-2 |
| 110℃，168 hr | -14 | % | IEC 811-1-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot press test | IEC 811-3-1 | ||
| penetration 6h at 100℃ | 9.0 | % | IEC 811-3-1 |
| penetration 6h at 90℃ | 5.0 | % | IEC 811-3-1 |
| Temperature index | 300 | ℃ | ASTM D2863 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.5E+12 | ohms·cm | DIN VDE 0303 |
| Dielectric constant | |||
| 50 Hz | 4.80 | IEC 60250 | |
| Dissipation factor | |||
| 50 Hz | 0.080 | IEC 60250 | |
| Conductivity | < 8.40 | µS/mm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 40 | % | ASTM D2863 |
| toxicity | 1.10 | NES 713 | |
| Smoke density | ASTM E662 | ||
| Flaming mode | 150 | ASTM E662 | |
| Non combustion mode | 290 | ASTM E662 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 4.50 | MPa | BS 6469 99.1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 53 | ISO 7619 | |
| tensile strength | 11.7 | MPa | IEC 811-1-1 |
| Tensile strain | |||
| fracture | 200 | % | IEC 811-1-1 |
| Abrasion | 181 | mm³ | VDE 0472 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 90 to 110 | °C | |
| Barrel 2 zone temperature | 105 to 125 | °C | |
| Barrel 3 zone temperature | 120 to 140 | °C | |
| Barrel 4 zone temperature | 120 to 140 | °C | |
| Barrel 5 zone temperature | 130 to 150 | °C | |
| Connector temperature | 135 to 155 | °C | |
| Head temperature | 140 to 160 | °C | |
| Nozzle temperature | 150 to 170 | °C | |
| Extruder screw length to diameter ratio L / D | 20.0:1.0 to 25.0:1.0 | ||
| Extruder screw compression ratio | 1.0:1.2 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 16h at 20°C, 500V |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |