| About |
|---|
| A fine powder normally pelleted and HF Preheated to give superior surface finish for such articles as tableware and ashtrays. Available in a wide range of colours. Suitable for food contact applications.&& |
| Product Description | |
|---|---|
| Generic | MF |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.52 | g/cm³ | ISO 1183 |
| Apparent density | 0.44 | g/cm³ | ISO 60 |
| Shrinkage rate | 3.5 | ISO 171 | |
| Shrinkage rate | ISO 2577 | ||
| — | 0.62 | % | ISO 2577 |
| — | 0.58 | % | ISO 2577 |
| Water absorption rate | |||
| Cold | 13.0 | mg | ISO 62 |
| Cold | 70.0 | mg | DIN 53472 |
| Hot | 50.0 | mg | ISO 62 |
| Post contraction | ISO 2577 | ||
| — | 0.85 | % | ISO 2577 |
| — | 1.1 | % | ISO 2577 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| bending strength | 119 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 2.2 | kJ/m² | ISO 180/C |
| Notched impact strength of cantilever beam | 9.8 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 186 | ℃ | ISO 75-2/Ae |
| Martens Temperature | 145 | ℃ | DIN 43458 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | IEC 60243-1 | ||
| — | 6.1 | kV/mm | IEC 60243-1 |
| — | 8.5 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | > 600 | V | IEC 60167 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| Extreme oxygen index | 44 | % | ISO 4589-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Preheated powder |
| 3. Cold powder |
| 4. 96 hr @ 23°C |
| 5. 24 hr @ 23°C |
| 6. 30 min @ 100°C |
| 7. (48 hr) Preheated powder |
| 8. (90°C) Preheated powder |
| 9. Procedure A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |