| About |
|---|
| Menzolit® SMC 0290 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn’t melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® SMC 0290 is a specially formulated SMC processable by injection moulding. The gentle production process prevents the fiber from any damage. Parts made of SMC 0290 reach higher levels of strength and stiffness than BMC types. Thus, the material is favoured in those fields of application where BMC doesn’t meet the demands regarding mechanical properties. SMC 0290 is serialized with a flammability of category V0 according to UL 94. Yellow Card is available for any tone! The glass content is on a level that combines good mouldability with good mechanical properties regarding strength and stiffness.&& |
| Product Description | |
|---|---|
| Generic | 热固性聚酯 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Low smoke,Halogen free,Flame Characteristics,High Heat Resistance,V-0 |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.70 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| — | 0.10 | % | ISO 2577 |
| — | 0.0 | % | DIN 53464 |
| Water absorption rate | |||
| Saturation, 23 ℃ | < 0.50 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| Compression Molding | 12000 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, molding | 60.0 | MPa | ISO 527-2 |
| Bending modulus | |||
| Compression Molding | 10000 | MPa | ISO 178 |
| bending strength | |||
| Compression Molding | 143 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| Compression Molding | 64 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | > 200 | ℃ | ISO 75-2/A |
| Continuous use temperature | 165 | ℃ | Internal Method |
| Glass transition temperature | 170 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD | 1.2E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | V-0 | UL 94 | |
| Igniting temperature of the hot wire | 960 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 32 | % | ISO 4589-2 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Glow Bar | Level BH 2 <= 10 | IEC 60707-3 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Mold temperature | 135 to 150 | °C | |
| Injection pressure | 8.00 to 10.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Post Molding Shrinkage |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |