About
Metocene HM562S is a metallocene-catalysed polymer with a very narrow Molecular Weight Distribution, suitable for extrusion application. It is formulated with an anti-gas fading stabilization package. It can be advantageously processed in different spinning technologies. Typical applications are spunbond nonwovens and continuous filaments such as partially-oriented yarns (POY). Metocene HM562S expands processing capabilities to achieve unmatched properties balances. It allows faster spinning and lower denier filaments. Additional advantages of Metocene HM562S are low volatiles and processing smokes.&&

About

Metocene HM562S is a metallocene-catalysed polymer with a very narrow Molecular Weight Distribution, suitable for extrusion application. It is formulated with an anti-gas fading stabilization package. It can be advantageously processed in different spinning technologies. Typical applications are spunbond nonwovens and continuous filaments such as partially-oriented yarns (POY). Metocene HM562S expands processing capabilities to achieve unmatched properties balances. It allows faster spinning and lower denier filaments. Additional advantages of Metocene HM562S are low volatiles and processing smokes.&&

Product Description
Supplier	LyondellBasell
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	High purity,Low smoke,Weight distribution,Solvent resistance,Homopolymer
Availabilitys	Africa & Middle East ,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Melt Flow Rate
230℃，2.16kg	30	g/10min	ISO 1133
Melt Volume Rate
230℃，2.16 kg	40.0	cm³/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	1450	MPa	ISO 527-2
tensile strength
Yield, 23 ℃	31.0	MPa	ISO 527-2
Tensile strain
Yield, 23 ℃	10	%
Fracture, 23 ℃	> 50	%
Bending modulus
23℃	1400	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	3.0	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	93.0	℃	ISO 75-2/B
Vicat Softening Temp
A50	136	℃	ISO 306/A50
B50	82.0	℃	ISO 306
Melting temperature
DSC	145	℃	ISO 3146

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.