Metton® LMR M2100V0

About
The Metton LMR reaction injection molding process can provide large parts in low pressure molds with the mechanical property performance similar to injection molded engineering thermoplastics. The combination of Metton LMR’s process and material capabilities result in a new design freedom for replacing traditional materials such as metal, wood and fiberglass. Fiber reinforced products tend to have poorer durability, but higher equivalent section modulus. In most semi-structural applications, Metton LMR can be designed to provide equivalent part stiffness for performance and generally at a significant weight reduction. This section contains polymer property data necessary to initially assess the compatibility of Metton LMR with a particular application. The Metton LMR product family includes a standard M15XX product line and a flame-retardant product which meets the requirements for classification as U.L. V-O. The Metton M15XX includes the products M1534, M1537, M1539 and M1540. The Metton V-0 product uses a special three stream RIM injection machine.&&

About

The Metton LMR reaction injection molding process can provide large parts in low pressure molds with the mechanical property performance similar to injection molded engineering thermoplastics. The combination of Metton LMR’s process and material capabilities result in a new design freedom for replacing traditional materials such as metal, wood and fiberglass. Fiber reinforced products tend to have poorer durability, but higher equivalent section modulus. In most semi-structural applications, Metton LMR can be designed to provide equivalent part stiffness for performance and generally at a significant weight reduction. This section contains polymer property data necessary to initially assess the compatibility of Metton LMR with a particular application. The Metton LMR product family includes a standard M15XX product line and a flame-retardant product which meets the requirements for classification as U.L. V-O. The Metton M15XX includes the products M1534, M1537, M1539 and M1540. The Metton V-0 product uses a special three stream RIM injection machine.&&

Product Description
Generic	DCPD
Material Status	Commercial: Active
Features	V-0
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.20	g/cm³	ASTM D792
Shrinkage rate
MD	0.70	%

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	1980	MPa	ASTM D638
tensile strength
yield	44.8	MPa	ASTM D638
Tensile strain
yield	4.0	%	ASTM D638
Bending modulus	2010	MPa	ASTM D790
bending strength
5% strain	74.5	MPa	ASTM D790
Poisson’s ratio	0.39

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ASTM D256
-40℃	53	J/m	ASTM D256
23℃	400	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed, 3.2 mm	105	℃	ASTM D648

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	V-0		UL 94

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.