MFE-2 is a bisphenol-A epoxy vinyl ester resin, offering excellent general properties, mechanical properties and corrosion resistance. PROPERTY Reliable process performance. Better resistance against acid and alkali. Lloyd’s Registered. Complies with FDA regulation 21 CFR 177.2420, when properly formulated and cured, for repeated use in food contact materials. APPLICATION Various types of anti-corrosive FRP products, chemical tank, pipe, marine/yachts, etc. Used in FRP protective surface of metallic or concrete structure Used as the jointing material of integral anti-corrosive resin-mortar flooring, granite and anti-proof brick, etc Can be used in filament winding, pultrusion, hand lay-up and spray-up process.&&

About

MFE-2 is a bisphenol-A epoxy vinyl ester resin, offering excellent general properties, mechanical properties and corrosion resistance. PROPERTY Reliable process performance. Better resistance against acid and alkali. Lloyd’s Registered. Complies with FDA regulation 21 CFR 177.2420, when properly formulated and cured, for repeated use in food contact materials. APPLICATION Various types of anti-corrosive FRP products, chemical tank, pipe, marine/yachts, etc. Used in FRP protective surface of metallic or concrete structure Used as the jointing material of integral anti-corrosive resin-mortar flooring, granite and anti-proof brick, etc Can be used in filament winding, pultrusion, hand lay-up and spray-up process.&&

Product Description
Supplier	Huachang
Generic	乙烯基酯
Material Status	Commercial: Active
Features	Alkali resistant,Corrosion Resistant,Food contact compliance,Acidproof
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
acid value	< 12.00	mg KOH/g
Solid content	57 to 63	%
viscosity
25℃	0.3 to 0.5	Pa·s

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	3500	MPa	ASTM D638
tensile strength	85.0	MPa	ASTM D638
Tensile strain
fracture	5.0	%	ASTM D638
Bending modulus	3300	MPa	ASTM D790
bending strength	140	MPa	ASTM D790

Supplementary information	Nominal value	Unit	Test method
Gel to Peak	5.0 to 10.0	min
exothermic peak	150 to 180	℃

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	110	℃	ASTM D648
thermal stability
80℃	> 1	day
Gelation time
25℃	10.0 to 20.0	min

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.