MFE® -7 - SOLIAO

About
MFE-7 is a bromated bisphenol-A epoxy vinyl ester with excellent fire retardancy. Both filled and non-filled fire-retardant epoxy vinyl ester resins are available based on MFE-7 resin. PROPERTY Excellent anticorrosion performance and mechanical function The oxygen index of FRP mixed with 3-5% Sb2O3 up to 40 Both casting and laminate meet ASTM E-84 Flame Spread “Class 1” rating. Good air drying APPLICATION Used in manufacturing fire-retardant and anti-corrosive FRP products and linings, also in surface coatings&&

About

MFE-7 is a bromated bisphenol-A epoxy vinyl ester with excellent fire retardancy. Both filled and non-filled fire-retardant epoxy vinyl ester resins are available based on MFE-7 resin. PROPERTY Excellent anticorrosion performance and mechanical function The oxygen index of FRP mixed with 3-5% Sb2O3 up to 40 Both casting and laminate meet ASTM E-84 Flame Spread “Class 1” rating. Good air drying APPLICATION Used in manufacturing fire-retardant and anti-corrosive FRP products and linings, also in surface coatings&&

Product Description
Supplier	Huachang
Generic	乙烯基酯
Material Status	Commercial: Active
Features	Corrosion Resistant,Flame Characteristics
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
acid value	8.00 to 16.00	mg KOH/g
Solid content	58 to 64	%

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	3500	MPa	ASTM D638
tensile strength	75.0	MPa	ASTM D638
Tensile strain
fracture	3.0 to 4.0	%	ASTM D638
Bending modulus	3500	MPa	ASTM D790
bending strength	130	MPa	ASTM D790

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	110	℃	ASTM D648
thermal stability
80℃	> 1	day

Thermosetting mixed viscosity	Nominal value	Unit
25℃	300 to 500	cP
Gelation time
25℃	15.0 to 25.0	min

Supplementary information	Nominal value	Unit
Gel to Peak	8.0 to 12.0	min
exothermic peak	150 to 180	℃
Sb2O3	3.0 to 5.0	%

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.