MFE® -W3 - SOLIAO

About
MFE-W3 is a novolac-based epoxy vinyl ester resin. It offers corrosion resistance at higher temperatures. PROPERTY High heat-resistance, heat distortion temperature of casting is 150°C and for FRP is 210°C. Excellent anti-corrosion and superior stability to some solvents and oxidizing media. Complies with FDA regulation 21 CFR 177.2420, when properly formulated and cured, for repeated use in food contact materials. APPLICATION Various corrosion resistant FRP products, such as chemical tank, pipe, served at elevated temperatures. Used as the jointing material, resin mortar and special adhesive with chemical resistance. Used as anti-corrosion FRP lining for the surface of metal or concrete. Can be used in pultrusion, filament winding, spray up and hand lay- up process.&&

About

MFE-W3 is a novolac-based epoxy vinyl ester resin. It offers corrosion resistance at higher temperatures. PROPERTY High heat-resistance, heat distortion temperature of casting is 150°C and for FRP is 210°C. Excellent anti-corrosion and superior stability to some solvents and oxidizing media. Complies with FDA regulation 21 CFR 177.2420, when properly formulated and cured, for repeated use in food contact materials. APPLICATION Various corrosion resistant FRP products, such as chemical tank, pipe, served at elevated temperatures. Used as the jointing material, resin mortar and special adhesive with chemical resistance. Used as anti-corrosion FRP lining for the surface of metal or concrete. Can be used in pultrusion, filament winding, spray up and hand lay- up process.&&

Product Description
Supplier	Huachang
Generic	乙烯基酯
Material Status	Commercial: Active
Features	Corrosion Resistant,Food contact compliance,High Heat Resistance,Inoxidizability,Solvent resistance
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
acid value	6.00 to 14.00	mg KOH/g
Solid content	62 to 68	%

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	3600	MPa	ASTM D638
tensile strength	80.0	MPa	ASTM D638
Tensile strain
fracture	3.5	%	ASTM D638
Bending modulus	3600	MPa	ASTM D790
bending strength	145	MPa	ASTM D790

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	150	℃	ASTM D648
thermal stability
80℃	> 1	day

Thermosetting mixed viscosity	Nominal value	Unit
25℃	250 to 350	cP
Gelation time
25℃	10.0 to 20.0	min

Supplementary information	Nominal value	Unit	Test method
Gel to Peak	5.0 to 10.0	min
exothermic peak	160 to 180	℃

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.